Two-component polyurethane sealant Oksiplast for seams, 12 kg Tenax

2 237

uah / set

Oksiplast is a high-quality two-component polyurethane sealant for sealing joints and cracks in vertical and inclined building structures.

It can be used for sealing joints in horizontal structures (floors) in the absence of mechanical load.
It is easily applied with a hand tool (for example, a spatula).
After mixing the components, it cures as a result of a chemical reaction.
The curing rate increases with increasing temperature.
After curing, the sealant has high tensile strength and excellent adhesion to the main building materials. It can be used in residential premises, provided that the sealant is fully cured before the start of operation of the premises.

High-quality two-component polyurethane sealant Oksiplast for sealing joints and cracks in vertical and inclined building structures.

Areas of application:

Sealing joints of vertical and inclined building structures
Sealing of seams and cracks in horizontal structures (floors) in the absence of mechanical load
Sealing of expansion joints with a maximum deformation of ± 25 %
Sealing of monolithic and precast reinforced concrete structures

Advantages:

Complies with EN ISO 11600 type F, class 25LM
Easy to use
Excellent thixotropy, does not flow in vertical seams
Good adhesion to concrete, metals and wood
Resistant to climatic factors, UV radiation
Retains elasticity over a large temperature range
Painted with acrylic paints

The device of the deformation seamTo prevent the formation of a third plane of contact of the sealant with the structural elements of the seam, it is always necessary to use anti-adhesive compounds or sealing gaskets, such as, for example, a bundle of foamed polyethylene.

We recommend selecting the size of the sealing gasket taking into account the actual width of the joint to limit the depth of the sealant layer, achieve the recommended ratio of width and depth of the sealant and reduce material consumption. In addition, the use of cellular sealing materials reduces the heat loss of the building.

It is necessary to follow the recommendations for the optimal width and depth of the seam for this sealant.

Applying the sealant with a layer thickness less than the minimum recommended leads to a decrease in the durability of the sealing seam.
Exceeding the maximum recommended thickness of the sealant layer causes high internal stresses that contribute to the appearance of cracks.

Custom Characteristics
Manufacturer Tenax
Country of origin	Latvia
Number of components	Two - component
Density	≈ 1.5 kg/liter
Shrinkage	≤ 3 %
Shore A Hardness	25 ÷ 35 after 28 days, at 23 °C and a relative humidity of 50 %
Seam width	from 10 to 50 mm
Appearance	White thixotropic mass, other colors are possible on request
modulus of elasticity at 100 % elongation	≤0.4 MPa
Elasticity	≥ 70 % (ISO 7389)
Packaging	The bulk (component A) is delivered in a plastic bucket, which also contains the hardener (component B) in a plastic container. It is completed in the ratio of components A: B, ready for direct mixing, namely 6: 1 by weight. The total weight of the kit is 12 kg.
Operating temperature range	from – 50 °C to 70 °C
Type of polymer	2-component polyurethane, cold curing after mixing the components under the influence of moisture
elongation at the moment of rupture	≥ 300 %
Conditional tensile strength	≥ 0.4 MPa
Seam depth	from 5 to 15 mm
Viability	≥ 5 hours (standard version), at 23 °C and 50% relative humidity ≥ 3 hours (winter version), at 23 °C and 50% relative humidity % Decreases with increasing temperature
Warranty period of storage	6 months in undamaged original packaging in dry warehouses at a temperature of no more than 30 °C.
Application temperature range	-15 °C to 30°C (standard version) -20 °C to 10 °C (winter version)
The ratio of the width to the depth of the seam	2:1
Permissible deformation	± 25 %